Interface effects between metal electrodes and organic films are crucial for the overall performance of organic electronics devices. We investigate effects from gold electrodes deposited on spin-coated films of poly(p-phenylene vinylene) (PPV). While a thin Au layer (16 nm) did not affect the absorption and emission spectra of PPV, a 64 nm thick Au layer induced blue shifts in both spectra owing to the reduction in the effective conjugation degree of PPV segments. Upon combining photoluminescence and Raman scattering spectroscopies, we noted that the Au clusters interact preferentially with the phenyl rings of the polymer chain, leading to shifts in the vibrational modes at 1100 and 555 cm-1 and a significant change in the electron-phonon coupling inferred from the Huang-Rhys parameters. These results are consistent with theoretical predictions in ab initiocalculations, which imply that the final properties of polymeric devices may be tuned with adequate conditions for electrode deposition.

In this report, we studied the thickness effect on the optical and morphological properties of self-assembled (SA) poly(p-phenylenevinylene) (PPV) films, wich were processed with 5 and 75 layers from a PPV precursor polymer and dodecylbenzenesulfonate, and then, thermally converted at 230 °C. The increase of the film thickness yielded more intense peaks in the vibrational spectral range. The electron-phonon coupling was quantified by the Huang - Rhys factor, that shows the effects on the polymer chain mobility in the interface substrate/polymer. A strong emission anisotropy r=0.57 was observed for the film with 5 layers of thickness decreasing to 0.34 for the film with 75 layers. Finally, the surface topology of the films was measured using Atomic Force Microscopy.

In this work we describe the processing of poly(styrene sulphonate) films (PSS) doped with neodymium (Nd). Optical density measurements in the UV-Vis-NIR region show the typical bands observed for neodymium chloride (NdCl3) in solution. In the case of films, the intensity ratio between the peaks at 800 nm (4I9/2 -> 4F5/2 + ²H7/2) and 580 nm (4I9/2 -> 4G5/2 + ²G7/2) is equal to 0.83. Infrared spectra present an enhancement in the absorption region of aromatic rings. Site selective luminescence spectroscopy shows that the incorporation of Nd introduces a hipsochromic shift and a line shape definition in UV luminescence compared to PSS film, decreasing the interaction between aromatic groups. In addition, the film exhibits an intense radiative transition at 1061 nm (4F3/2->4I11/2), comparable to the one present in crystalline materials doped with Nd.

A study is presented of the formation and optical properties of polymeric heterostructures from poly(p-phenylene vinylene) (PPV) and poly(o-methoxyaniline) (POMA) produced via the self-assembly technique. POMA layers were obtained in a non self-limiting process from its emeraldine salt, semiconducting form in HCl solution. Thermal conversion of PPV was performed at low temperatures with the substitution of the counter-ion Cl in the PPV precursor by a long sulfonic chain, the dodecylbenzenesulfonate (DBS) ion. The optical properties of PPV films converted in this way are not affected by POMA, which can be used as transparent electrode of PPV luminescent devices.